Belzona Restores Japanese Aluminum End Covers
Severe erosion caused by a combination of corrosive environment and abrasion of a fanbelt.
CASE
Protection of Stainless Steel Scrubber Vessel from Chemical Attack
Problem
Newly fabricated stainless-steel scrubber vessels were put in service without a coating thinking the stainless-steel will provide enough protection. After 3 months they were having through wall defects in several parts of the vessel.
Industry
Water & Wastewater Management
Application Date
2022
Location
Ontario / Canada
Equipment Application
TCC-Tanks and Chemical Containment Areas
Subtrate
Stainless Steel
Product
Belzona 1111 (Super Metal)
Belzona 4311 (Magma CR1)
Repair Stages
Application Situation
They had already invested in the fabrication of 4 of these vessels, so they needed to do something to protect their investment. The surface area that needed to be protected was around 2000 sq.ft per vessel. The contents in the vessel were very acidic and it got more concentrated at the bottom of the scrubber which is where they had the most problems.
Application Method
The whole vessel was grit blasted. They had welds and irregular surfaces which were smoothed and filled with Belzona 1111. Then Belzona 1111 was frost blasted and two coats of Belzona 4311 were applied.
Belzona Facts
We were able to secure the job as we created coated samples for the customer and sent them for immersion testing. The product performed well so they decided to proceed with the application. The vessel was opened after 3 months and then after 1 year and the coating was still in good shape protecting the vessel.
Contact your nearest Belzona Consultant and schedule a free evaluation!
Other Cases
Belzona 1812 Protects Newly Fabricated Screw Conveyor
Replacing fast depleting screw conveyors in service is hard. So, customer decided to protect and put to test a newly fabricated screw conveyor coated with Belzona 1812 against the abrasive conditions in the plant.
Belzona Restores Japanese Aluminum End Covers
Severe erosion caused by a combination of corrosive environment and abrasion of a fanbelt.