With a wide range of case studies featuring different industries, equipment, products and more with hands on solutions provided.
Newly fabricated stainless-steel scrubber vessels were put in service without a coating thinking the stainless-steel will provide enough protection. After 3 months they were having through wall defects in several parts of the vessel.
Hydrochloric acid tank in a Pickle line was suffering from chemical attack and developed a leak. They needed a product that had excellent chemical resistance against Hydrochloric acid at high concentrations to stop this leak and protect the outside of the tank.
Customer was having a problem with leaking heat exchanger plates due to corrosion.
Customer had a new tank and wanted to protect the inside with a lining that would protect it from 75% Phosphoric acid thereby extending its service life.
1 inch steel pipe had corrosion and was leaking at the pipe seam and socket weld joint.
The internal walls of the salt hopper were suffering from corrosion and salt would not flow to the screw auger at the bottom.
1 inch steel pipe had corrosion and was leaking at the pipe seam and socket weld joint.
The secondary clarifiers at the Water Pollution Control Center were pitted and deteriorated due to chemical attack from the biological treatment process.
Internal corrosion had led to water leaks and these were finding there way through to the floor below.
Water was collecting on this large reinforcement seam causing extensive corrosion.