With a wide range of case studies featuring different industries, equipment, products and more with hands on solutions provided.
The centrifuge was suffering from erosion-corrosion and scale buildup. They needed a product that would protect the equipment but also help reduce the buildup and improve the efficiency of the equipment
A municipality discovered a perforation in a carbon steel pipe feeding a pressure vessel containing granular activated carbon. The pipe, which conveys potable water with 4 ppm hydrogen peroxide, had suffered coating failure and internal corrosion. With the system needing to be operational within two weeks, the municipality sought a repair method that would minimize downtime and avoid hot work, while being suitable for continuous immersion in drinking water.
Tank was very badly corroded and required refurbishment and protection.
Through wall defect and wear in pump caused by sewage and particles in wastewater was to be repaired and lined with intention of getting more lives out of the pumps.
Pipe elbows had a concrete liner which was very deteriorated and at times concrete chunks became loose in the system which was unacceptable.
The pipe section was suffering from general external corrosion. The pipe had become weakened from severe metal loss. This pipe section never got flooded nor exposed to immersion conditions. Yet, there was a lot of moisture in the environment.
Newly fabricated stainless-steel scrubber vessels were put in service without a coating thinking the stainless-steel will provide enough protection. After 3 months they were having through wall defects in several parts of the vessel.
Weld Joint on stainless steel pipe was leaking due to a porosity and slag inclusion.
The existing pipe had become severely weakened over time and they needed to reinforce it to prevent future problems.
Diffuser ring was corroded and certain areas were worn out and needed to be resurfaced.